Water Resistance Acrylic Emulsion Counterpart To Joncryl 624 For Flexo Plastic Varnish

Brand Name : WeiLi Resin®

Model Number : WQ-2015

Certification : ISO9001

Place of Origin : China

MOQ : 5000KG

Price : Negotiable

Payment Terms : L/C, T/T

Supply Ability : 500t/month

Delivery Time : 14 work days

Packaging Details : 200kg/drum

Appearance : Milkywhite

Solid Content : 50±1%

PH(25℃) : 8.0-9.0

Acid Value : 50

Viscosity : 1800-3000mPa*s

Tg : -23℃

Package : 1000kg or 200kg

Contact Now

Water Resistance Acrylic Emulsion Counterpart To Joncryl 624 For Flexo Plastic Varnish

Introduction

WQ-2015 acrylic emulsion has excellent water and rub resistance and film wetting and good ddhesion to lots of substrates. It is specially designed for flexo & gravure plastic inks and overprint varnishes. It promotes gloss, holdout, and resolubility in printing ink and overprint varnish formulations and can also be used to produce inorganic and organic pigment dispersion.

It is recommended to use WQ-2015 water based acrylic emulsion and WQ-2011 non-filming acrylic emulslion for water based flxography plastic varnish. The final inks will have excellent water resistance and rub resistance.

Physical Property:

Appearance Milky white
Solid Content (%) 49±1
Acid Value 50
Viscosity(mPa*s) 1800-3000
PH(25℃) 8.0-9.0
Tg(℃) -23
MFFT(℃) <0

Rerefence Formulation For Water Based Varnish For Plastic Substrate (Flexography)

No. Raw Materials %
① WQ-2015 (film-forming) 70.00
② WQ-2011 (non-film forming) 19.00
③ WQ-2028 (improving gloss) 5.50
④ Wax emulsion 4.00
⑤ DOWSIL™ 51 : Ethanol (1:1) * 1.00 Dow Corning
⑥ Defoamer 0.50 TEGO Foamex 825
Total 100.00
Remark:
1. ①＋②＋③+④+⑤＋⑥
Add the above materials and stir at the same time, at a constant speed, stirring time: about 30 minutes/300 rpm.
2. *: DOWSIL™ 51 Additive diluted with Ethanol =1:1
3. 4# cup: 25 seconds ± 2
PH value: 8.20 ± 0.5%
4. Final inks: varnish 70%+pigment paste 30% =100 (Ajusting it accoring to needs)

Performance:

  • Self-closslinking and Excellent film-forming
  • High adhesion force
  • High resistance to water, Oil.
  • High friction coefficient

Water Resistance Acrylic Emulsion Counterpart To Joncryl 624 For Flexo Plastic Varnish

Storage

The product should be stored in a closed container to avoid freezing and high temperature. Suggested normal storage temperature is 10 to 35℃.

Packing

200kg small mouth plastic drum

Water Resistance Acrylic Emulsion Counterpart To Joncryl 624 For Flexo Plastic Varnish

Special Tips

This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.


Product Tags:

Milkywhite Water Resistant Acrylic Emulsion

      

Flexo Plastic Varnish Acrylic Emulsion

      

Joncryl 624 Water Based Acrylic Resin

      
Wholesale Water Resistance Acrylic Emulsion Counterpart To Joncryl 624 For Flexo Plastic Varnish from china suppliers

Water Resistance Acrylic Emulsion Counterpart To Joncryl 624 For Flexo Plastic Varnish Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Xiamen WangQin Chemical Technology Co., Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You May Like